Home » Ceramic Parts

Ceramic Parts

Ceramic Parts

Material:
Alumina(Al2O3)96%-99%
Zirconia (ZrO2)

Process:
Ceramic Injection Molding
Dry Pressing

Material
Composition
Typical Properties
Grain Size (μm)
Density (g/cm³)
Electrical R (Ω-m)
Rupture Strength (MPa)
Hardness (HV300gf)
Pure Alumina
AI2O3
<3
3.95
>10¹³
400
2000
98% Alumina
AI2O3
<5
3.88
>10¹³
275
1900
Zirconia
ZrO2
<0.6
6.05
>10¹²
700
1200
Toughened Alumina
AI2O3+ZrO2
<1
4.15
>10¹³
550
1850
Stabilized Zirconia
ZrO2+Y2O3
<0.8
5.55
>10¹³
900
1350